由于铸铜件存在疏松多孔的金属结构,在电镀过程中,须严格工艺要求:
1.镀银时,必须带电下槽,采用冲击电流密度在摇动工件的前提下电镀5min,然后再转为正常电流密度.
2.镀银后的钝化处理要加强清洗,在流动清水中冲10~20min,再用热水洗,马上干燥,烘箱温度可控制100~150℃,时间稍长一点,以防产生霉点。
3.各道工序的清洗要,防止残留在孔隙中的溶液影响下道工序;
4.铸铜件实际表面积比计算的表面积大许多倍,电镀时冲击电流密度比一般零件高3倍左右,预镀的时间也比一般零件长一些。
![](https://img73.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f91a89452dc4b35a20777429e22a88e916.jpg)
![](https://img77.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f916509f91c21038c6cc799f895a0ae9a9.jpg)
![](https://img79.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f9c81665c61fd6161870ef3113cf946fe0.jpg)
![](https://img71.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f9fb18f8005062430c6b93ff5795a40658.jpg)
![](https://img72.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f9f77002e60d630e76afe4d8731e9d0e56.jpg)
![](https://img71.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f94c4a65d42d892c651276857a833ed8b5.jpg)
![](https://img72.gc1288.com/5eceadd4559dcfd2d42aff014738af105b9952c86917a5f9ab71bba40be9a1227561dadc9626e457.jpg)
泊头市河铸重工机械有限公司
免费会员
Product Display
由于铸铜件存在疏松多孔的金属结构,在电镀过程中,须严格工艺要求:1.镀银时,必须带电下槽,采用冲击电流密度在摇动工件的前提下电镀5min,然后再转为正常电流密度.2.镀银后的钝化处理要加强清洗,在流动清水中冲10~20min,再用热水洗,马上干燥,烘箱温度可控制100~150℃,时间稍长一点,以防产生霉点
由于铸铜件存在疏松多孔的金属结构,在电镀过程中,须严格工艺要求:
1.镀银时,必须带电下槽,采用冲击电流密度在摇动工件的前提下电镀5min,然后再转为正常电流密度.
2.镀银后的钝化处理要加强清洗,在流动清水中冲10~20min,再用热水洗,马上干燥,烘箱温度可控制100~150℃,时间稍长一点,以防产生霉点。
3.各道工序的清洗要,防止残留在孔隙中的溶液影响下道工序;
4.铸铜件实际表面积比计算的表面积大许多倍,电镀时冲击电流密度比一般零件高3倍左右,预镀的时间也比一般零件长一些。
请选择省份
请输入账号
请输入密码
请输验证码
全球工厂网 设计制作,未经允许翻录必究 .Copyright(C) https://www.gc1288.com,All rights reserved.
以上信息由企业自行提供,信息内容的真实性、准确性和合法性由相关企业负责,全球工厂网对此不承担任何保证责任。
所有评论仅代表网友意见,与本站立场无关。