MIG焊丝
| 类别 | 品名 | AWS型号 | 熔敷金属化学成分(%) | 熔敷金属力学性能 | 保护气体 | 简明与用途 | ||||||||
| C | Mn | Si | Cr | Ni | 其它 | σ0.2 (MPa) | δb (MPa) | δ (%) | IV (J) | |||||
| M I G 焊 丝 | MG-1CM | ER80S-G | 0.07 | 1.06 | 0.56 | 1.32 | - | Mo:0.57 | 510 | 630 | 23 | 0℃/88 | CO2 | 1~1.25%Cr-0.5%Mo耐热钢CO2焊接用。 |
| MGS-2CM | ER90S-G | 0.10 | 1.22 | 0.32 | 2.31 | - | Mo:1.01 | 580 | 690 | 23 | 0℃/78 | CO2 | 2.25%Cr-1%Mo耐热钢CO2焊接用。 | |
| MGS-1CM | ER80S-G | 0.07 | 0.74 | 0.34 | 1.23 | - | Mo:0.52 | 570 | 680 | 22 | 0℃/69 | Ar+2-5%O2 99% CO2 | 1~1.25%Cr-0.5%Mo耐热钢，短路电弧焊接用 | |
| MGT-1CM | ER80S-G | 0.05 | 0.68 | 0.45 | 1.27 | - | Mo:0.54 | 460 | 580 | 27 | 0℃/140 | Ar+2%O2 99% CO2 | 1~1.25%Cr-0.5%Mo耐热钢，短路电弧焊接用 | |
| MGT-2CM | ER90S-G | 0.08 | 0.76 | 0.34 | 2.29 | - | Mo:0.98 | 550 | 670 | 26 | 0℃/110 | Ar+2-5%O2或 Ar+5-20%CO2 | 2。25~1%Mo耐热钢，喷射电弧焊接用 | |
| MGT-2CM | ER90S-G | 0.07 | 0.75 | 0.43 | 2.31 | - | Mo:0.99 | 550 | 680 | 23 | 0℃/130 | Ar+2%O2 99%CO2 | 2.25~1%Mo耐热钢，短路电弧焊接用 | |
| MGS-5CM | ER80s-B6 | 0.08 | 0.56 | 0.29 | 5.46 | - | Mo:0.53 | 480 | 640 | 26 | 0℃/78 | Ar+2-5%O2或 Ar+5-20%CO2 | 5%Cr-0.5%Mo耐热钢，喷射电弧焊接用 | |
| MGS-9CM | ER80S-B8 | 0.08 | 0.49 | 0.38 | 9.01 | - | Mo:1.04 | 480 | 640 | 24 | 0℃/130 | Ar+2-5%O2或Ar+5-20CO2 | 9%Cr-1%Mo耐热钢，喷射电弧焊接用 | |
| MGS-9Cb | ER90S-G | 0.08 | 1.29 | 0.27 | 8.86 | 0.38 | Mo0.98 Nb0.03V0.19 | 480 | 640 | 24 | 0℃/98 | Ar+5%CO2 | 9%Cr-1%Mo-Nb-V耐热钢，喷射电弧焊接 | |